Abstract: This research studied the recycling of borosilicate glass wastes from damaged laboratory glassware. The luminescent glasses were prepared by doping glass waste powder with rare earth ions, namely, dysprosium ions (Dy3+) and samarium ions (Sm3+), as well as co-doping with Dy3+ and Sm3+ at a concentration of 2% by weight. The sintering process was conducted in a microwave oven for a duration of 15 min. The photoluminescence spectra of the doped glasses were obtained under excitation at 401 nm and 388 nm. The results showed that the emission characteristics depended on the doping concentrations of Dy3+ and Sm3+ and the excitation wavelengths. Upon excitation at 401 nm, the co-doped glasses exhibited the maximum emission peak of Sm3+ at 601 nm (yellowish and orange region in the CIE chromaticity diagram) due to the energy transition from 4G5/2 to 6H7/2. When excited at 388 nm, however, the emission spectra of the co-doped glasses were similar to the characteristic emission peaks of Dy3+ (white region in the CIE chromaticity diagram), but the peak position exhibits a red shift. This could be attributed to an increase in the amount of non-bridging oxygens (NBOs) by co-doping.
Source: Journal of Composites Science
DOI: 10.3390/jcs9020064
Institution: Silpakorn University
Language: English
Subfield: Ceramics and Composites
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,172
OpenAlex ID: W4407088778