Above-bandgap and sub-bandgap photoelectron emission from diamond‑silver nanocomposite thin films
Year: 2025
Type: article
Abstract: Recent studies have demonstrated that the introduction of silver nanoparticles into semiconducting films increases their electron emission characteristics and their ability to catalyzing chemical reduction reactions. This study investigates the impact of silver nanoparticles on the electron emission characteristics of diamond thin films. Ag nanoparticles were produced by thermal evaporation onto H-terminated surfaces of freshly grown diamond thin films produced by plasma-enhanced chemical vapor deposition and were then encapsulated using another stage of seeding and diamond growth. The energy distribution of the emitted electrons was characterized when illuminated with sub-bandgap light sources at 261 nm (4.75 eV) and 405 nm (3.05 eV) and with above-band light at 21.2 eV. At 261 nm the diamond-Ag-diamond structures increase photoelectron yield by approximately 3× compared with freshly H-terminated diamond, while at 405 nm the yield is increased approximately 200-fold. Our results suggest that the encapsulated Ag nanoparticle likely increase the yield through a combination of effects, including increasing the amount of sp 2 -hybridized carbon in the near-surface region, charge equilibration at the Ag-diamond interface, and increased scattering in the near-surface region, thereby increasing the effective optical absorption close to the diamond surface. • Diamond‑silver nanocomposites increases sub-bandgap electron yield 200-fold at 405 nm. • Diamond-Ag-Diamond structures lower electronic kinetic energy by 1 eV e. • Etching away the silver shifts reduces the emission intensity. • Diamond-Ag-Diamond structures have increased sp2-hybridized carbon. • Mechanism involves both Ag-diamond band alignment and increased non-dimaond carbon.
Source: Diamond and Related Materials
Authors: Anand B. Ode, Robert J. Hamers
Institution: University of Wisconsin–Madison
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $2,690
Award: G120504136
OpenAlex ID: W4407761579