Optimizing the photodegradation process of low-density polyethylene using Taguchi's robust statistical design

Year: 2025

Type: article

Abstract: The present study employs the Taguchi statistical design for optimizing the photodegradation process of low-density polyethylene (LDPE) films by varying five significant parameters i.e., catalyst loading (%), exposure time (in days), pH, size of the films (cm x cm), and temperature (℃), simultaneously to determine the maximum photodegradation on LDPE. The physiochemical, morphological, and molecular structural changes were observed in all-nanocomposite (LDPE and catalyst samples) before and after degradation. One way-ANOVA (Analysis of Variance) results demonstrated that catalyst loading, and exposure time were the most influential factors and contributed 65 % and 25 %, respectively to determine the degradation rate. Further, a kinetic study was performed to determine the photo-degradation rate, and it follows first-order photo-kinetics model. The maximum photodegradation was observed for that LDPE sample that was loaded with 12 % catalyst with a pH of 6 at 45°C that was exposed to the UV light for 10 days in a photoreactor, it degraded most efficiently with a weight loss of 16.25 %. Additionally, recyclability studies confirmed that stability and reusability of TiO 2 as a photocatalyst for carrying out degradation experiments upto three consecutive cycles. Moreover, there is a high co-relation between predicted and experimental data with R 2 > 0.96, which demonstrates the effectiveness of the prediction with the maximum degradation of LDPE film. • Taguchi method is employed for optimizing photodegradation on LDPE-TiO 2 films. • Photo-degradation is prioritization as catalyst loading> time > pH > temperature > size. • Maximum weight loss and degradation rate were 16.25 % and 5.76 %, respectively. • Recyclability studies demonstrated that TiO 2 photocatalyst is stable upto three cycles.

Source: Next Materials

DOI: 10.1016/j.nxmate.2025.100562

Authors: M.S.S.R. Tejaswini, Pankaj Pathak

Institutions: Vignan's Foundation for Science, Technology & Research, SRM University, Andhra Pradesh

Language: English

Topic: TiO2 Photocatalysis and Solar Cells

Subfield: Renewable Energy, Sustainability and the Environment

Field: Energy

Domain: Physical Sciences

SDG: Responsible consumption and production

Open Access status: gold

Estimated APC paid: $1,280