Advancement in tribological performance of hexagonal Bi2Te3 nanosheets by incorporation of Ag2MoO4 nanoparticles

Year: 2025

Type: article

Abstract: The hydrothermal, and co-precipitation methods were used to synthesize bismuth telluride (Bi 2 Te 3 ) nanosheets, and silver molybdate (Ag 2 MoO 4 ) nanoparticles, respectively to improve the tribological activity of lubricating oil. Being a hexagonal 2D structure, Bi 2 Te 3 nanosheets are considered to be tribologically active. With a purpose to have the tribological activity of high order, an attempt has been made to decorate Bi 2 Te 3 nanosheets with Ag 2 MoO 4 nanoparticles in the form of nanocomposite Ag 2 MoO 4 /Bi 2 Te 3 . The morphological analysis of Ag 2 MoO 4 /Bi 2 Te 3 nanocomposites using HR-SEM, TEM, and HR-TEM, confirms a uniform distribution of nanoparticles throughout the Bi 2 Te 3 nanosheets. The tribological efficacy of the extensively analyzed nanomaterials was assessed in base lube (paraffin oil) at an optimized concentration, 0.03 % w/v, employing a four-ball tester executing ASTM D4172 and ASTM D5183 tests. Based on the analyzed tribological data, mean wear scar diameter (MWD), coefficient of friction (COF), and seizure load, synthesized nano additives exhibited superior tribological performance compared to the base oil. The antiwear and antifriction efficiency was found in the following order- Ag 2 MoO 4 /Bi 2 Te 3 ≫ Ag 2 MoO 4 > Bi 2 Te 3 , and Ag 2 MoO 4 /Bi 2 Te 3 ≫ Bi 2 Te 3 > Ag 2 MoO 4 , respectively. The nanocomposites demonstrated significantly enhanced tribological activity attributable to the synergistic interaction between noncovalently bonded nanosheets and nanoparticles. All constituent elements, elemental composition, and metal oxides (Bi 2 O 3 , TeO 2 , Ag 2 O, MoO 3 , MoO 2 , and Fe 2 O 3 ) formed in the tribofilm, have collectively contributed to the lubrication, were validated through energy-dispersive X-ray spectroscopy (EDX) and XPS techniques. The SEM and AFM investigations of the lubricated surface verified the result of antiwear and antifriction. The graphical abstract represents the TEM images of synthesized nanoadditives and their tribological performances using a Four-Ball lubricant tester.

Source: Hybrid Advances

DOI: 10.1016/j.hybadv.2025.100429