Effects of a Welding Wire Containing Er or Sc on the Microstructure, Mechanical Properties, and Corrosion Resistance of the 5xxx Aluminum Alloy MIG Joint
Year: 2025
Type: article
Abstract: The development of MIG (metal inert gas) welding for five-series aluminum alloys primarily involves the improvement and optimization of welding processes. Building upon research findings regarding the enhancement of aluminum alloy properties through the use of scandium (Sc) and erbium (Er), our study incorporates Sc and Er into the welding wire to examine their impact on welding quality. The results show that the introduction of Er and Sc results in grain refinement from 47 µm to 29 µm and 31 µm, respectively. Grain refinement is mainly attributed to the heterogeneous nucleation of submicron-sized, coherent Al3Er and Al3Sc phases with L12 structure. The ultimate tensile strength (UTS), fracture elongation EI [%], and microhardness of joints welded with Er-containing and Sc-containing filler wires exhibit significant enhancements due to the refinement strengthening and dispersion strengthening. Joints welded with the filler wires containing Er and Sc display reduced corrosion current density and higher corrosion potential. The enhanced corrosion resistance comes from the formation of a denser oxide film and the equilibrium in the potential difference between the precipitated phases (Al3Er and Al3Sc) and the matrix. Filler wires containing Er and Sc have almost similar effects on improvements of the MIG welding joints.
Source: Metals
DOI: 10.3390/met15030287
Authors: Cunwei Zou, Ruizhi Wu, Xinhe Yang, Zhikun Ma, Legan Hou
Language: English
Subfield: Aerospace Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
Awards: G1749874758, G3771363677, G5201856085
OpenAlex ID: W4408201982