Effect of carbon content on microstructure and tensile properties of Ni-based GH3230 superalloy
Year: 2025
Type: article
Abstract: This present work investigates the dependence of carbon (C) content variation (0.074 wt%, 0.1 wt%, 0.15 wt%) on the microstructure and tensile properties of GH3230 superalloy at 23 °C and 950 °C. The results show that the variation in C content did not change the type of precipitated particles, and all the variants included M 6 C and M 23 C 6 . Moreover, the increase in C content preferred to increase the volume fraction of M 23 C 6 and promoted the formation of clusters within the grains as well as the formation of lamellae or films at grain boundaries. The tensile properties at 23 °C indicated that the increase in C content significantly improved the yield strength (YS), and the evaluation of the strengthening mechanism revealed that the contribution of carbide particle strengthening was the main reason for the strength enhancement. Meanwhile, due to the dual effects of uniform carbide distribution and grain refinement, the plasticity peaked at the C content of 0.1 wt%. At 950 °C, the strengths of the three C content variants remained at similar levels, and the plasticity declined severely with the increase in C content. Fracture characterization revealed that the increase in C content accelerates the dynamic recovery and dynamic recrystallization (DRX) process. The grain boundary weakening effect of fine DRX grains and the increase of the phase interface between DRX grains and high-volume fraction carbides accelerate the stress concentration and crack development, which leads to the severe reduction of plasticity.
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,640
OpenAlex ID: W4408201987