Abstract: This study explored the effects of varying silicon content on the microstructure, hardness, and toughness of gray cast iron. Gray cast iron samples with silicon compositions of 2.466, 2.981, 3.304, and 3.363 wt% were subjected to metallographic analysis, hardness testing, and toughness testing to assess the impact of silicon variation. The microstructural analysis, conducted using Scanning Electron Microscopy (SEM), revealed that increasing the silicon content resulted in the thickening of graphite flakes and a corresponding reduction in pearlite content. This microstructural change led to a decrease in the hardness of the material, as shown by a decline in Brinell hardness numbers from 343.728 to 205.498 BHN. In contrast, the toughness of the gray cast iron improved with increasing silicon content, with Charpy impact values rising from 0.058 to 0.066 Joule/mm2 across the same range. These findings indicate that while higher silicon content enhances the toughness of gray cast iron, it simultaneously reduces its hardness, suggesting a trade-off between these critical mechanical properties. This study provides valuable insights for designing and optimizing gray cast iron with tailored mechanical properties, particularly for applications where increased toughness is desirable. Further research is recommended to explore a wider range of silicon content and the potential effects of other alloying elements on gray cast iron’s performance.
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W4408418604