Combustion Profile of Bio-pellet Produced from Sawdust Using Wet Torrefaction Method with Various Concentrations of Acetic Acid
Year: 2025
Type: conference-paper
Abstract: Sawdust is one of the industrial wastes which naturally contains low energy density. An effective method is needed to utilize this biomass as a solid fuel product. This work aimed to investigate the physical and combustion properties of bio-pellets produced from sawdust under the wet torrefaction method. To prepare sawdust bio-pellet a number of steps were carried out including the wet torrefaction process, dough preparation, pelletizing, and drying. Wet torrefaction was performed by hydrothermally treating the sample in an autoclave at a temperature of 130°C and pressure of 2 atm (g) for 80 minutes. For the hydrothermal process, the used acetic acid solution was varied with variations of 1.3 M, 1.8 M, and 2.3 M. Properties of the product were analyzed under proximate and bomb calorimetry analyses. To evaluate the combustion properties a purposely built test apparatus was developed equipped with a data logger system. Based on the results it can be observed that increases in torrefaction temperature and acetic acid concentration resulted in an increase in the calorific value as well as decreases in the ash content. The highest calorific value was 4745 kcal/kg obtained from sawdust torrefied in acetic acid with a concentration of 2.3 M at a temperature of 130°C. This sample also exhibits the lowest ash content which is only 1.97%. The combustion test disclosed a maximum combustion temperature of 589°C with a burning rate of 0.711 g/min. Overall, the wet torrefaction applied in this investigation was beneficially enhanced the properties of bio-pellet products.
Authors: Indah Ayu Pertiwi, Muhammad, Abubakar, Adi Setiawan, Rizky Iskandar
Institution: Malikussaleh University
Language: English
Subfield: Biomedical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W4408418622