Adsorption Efficiency of UV-Irradiated Polyvinyl Alcohol-Alginate Adsorbent Beads for Chromium (VI) Removal
Year: 2025
Type: article
Abstract: Due to the risk of chromium (Cr) contamination, industrial waste emissions have become a global concern, necessitating an effective adsorption approach.Polyvinyl alcohol (PVA) -alginate beads are a promising material for overcoming this problem.The present work aims to investigate the effect of ultraviolet (UV) light irradiation on the preparation of PVA-alginate beads throughout a range of UV irradiation durations, as well as its Cr (VI) removal rate.In this work, a homogeneous gel made of PVA and sodium alginate (SA) was produced and then radiated to UVA light for varying periods of time (5-20 minutes).Subsequently, the PVA-alginate adsorbent beads were made by crosslinking with 6% boric acid and 2% calcium chloride.PVAalginate adsorbent beads were fabricated easily after UVA irradiation because the viscosity of gel PVA-alginate was reduced.The Cr (VI) adsorption experiment employed 15 g of PVA-alginate adsorbent beads, 180 minutes of adsorption time, and 50 mg/L Cr (VI) initial concentration.The size analysis revealed that the average diameter of the adsorbent beads after Cr (VI) adsorption was approximately 4.00 mm.The UV-Vis results showed that sample A prepared by exposing the PVA-alginate adsorbent beads to UV light for 5 minutes has an optimum Cr (VI) removal rate of 71.63% after in contact for 180 minutes.This study's findings were critical for establishing a new knowledge of the production of PVA-alginate beads irradiated with UV light and moving forward to mitigate heavy metal pollution in waste water, therefore enhancing the quality of water and the environment.
Authors: Universiti Tun Hussein Onn Malaysia (UTHM), W.G. Lau, M.A. Selimin, Universiti Tun Hussein Onn Malaysia (UTHM), T.C. Lee, Universiti Tun Hussein Onn Malaysia (UTHM)
Institution: Tun Hussein Onn University of Malaysia
Language: English
Subfield: Water Science and Technology
Field: Environmental Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W4408461998