Thermally induced PtOx interfacial layer enhances stability of Pt/β-Ga2O3 vertical Schottky diodes

Year: 2025

Type: article

Abstract: This study investigates the long-term stability of Pt/β-Ga2O3 field-plated Schottky barrier diodes at high temperatures, with extended thermal cycling and soaking stress. The device characteristics reveal a strong dependence on operating temperature, leading to an ON/OFF current ratio of ∼10× at ±3 V and 600 °C. Extensive thermal cycling (25 cycles over 100 h) between room temperature and 350 °C shows that leakage currents stabilize after the initial ten cycles. This stabilization is likely due to the formation of a thin PtOx layer at the Pt/β-Ga2O3 interface, as confirmed by high-resolution scanning transmission electron microscopy. Further exposure to a constant 350 °C environment for 10 h reveals a slight increase in the leakage current from 10−7 to 10−6 A at −5 V and degradation of the forward current, due to potential thermodynamic instability of the Ohmic contacts. This study provides insights into the changes in the Pt/β-Ga2O3 diode performance with thermal stress, offering a basis for predicting the device’s operational reliability at high temperatures for sensing and power applications.

Source: APL Energy

DOI: 10.1063/5.0251435