Microstructure and mechanical properties of multidirectionally forged Al alloy 1570С subjected to cryogenic rolling

Year: 2025

Type: article

Abstract: The effect of cryogenic rolling at -196°C up to 90% reduction on the microstructure and static strength of a 1570C alloy (Al-5.0Mg-0.18Mn-0.2Sc-0.08Zr-0.01Fe-0.01Si wt%), pre-processed by multidirectional isothermal forging (MIF) at 325°C to a total strain of about 12, is investigated. MIF of the homogenized ingot allowed to obtain a near-homogeneous (ultra)fine grained (UFG) structure with a grain size of 2.3 μm, leveled Mg in solid solution and a uniform distribution of second phases, which ensured subsequent rolling without cracking. Rolling transformed the forged structure into a pancaked (flattened) UFG high work-hardened structure with a halved fraction of high-angle boundaries, characterized by a dislocation density of 10 15 m -2 and a partially developed nano-sized crystallite structure with a coherent domain size of 15 nm. These structural changes resulted in significant improvements in room temperature tensile strength compared to the initial homogenized/forged conditions: yield strength increased from 245/235 to 590 MPa and ultimate tensile strength increased from 355/365 to 620 MPa, while elongation decreased from 26/37 to 9%. The increase in strength with reduced ductility is attributed to the superposition of grain boundary and dislocation strengthening mechanisms amid dispersion strengthening. Therewith, cryogenic rolling promotes uniform dislocation structures and a homogeneous distribution of Al 3 (Sc,Zr) precipitates, which interact with the dislocations to maintain relatively high ductility even in a highly deformed state.

Source: International Journal of Lightweight Materials and Manufacture

DOI: 10.1016/j.ijlmm.2025.03.005

Authors: Oleg Shamilevich Sitdikov, Elena Viktorovna Avtokratova, Rinat Rustemovich Zagitov, Oksana Eduardovna Latypova, Stanislav Vatslavovich Krymskiy, Mikhail Vyacheslavovich Markushev

Institutions: Russian Academy of Sciences, Institute of Metal Superplasticity Problems

Language: English

Topic: Aluminum Alloy Microstructure Properties

Subfield: Aerospace Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: diamond

Funder: Russian Science Foundation

Award: G8347236992