Study of the Effect of Bi and Ce Doping on the Performance of the VWTi Catalyst for Reduction of Nitrogen Oxides
Year: 2025
Type: article
Abstract: Ce‐doped V 2 O 5 ‐WO 3 /TiO 2 (CeVWTi) and its subsequent modifications have been recognized as effective catalysts for the selective catalytic reduction of NO. Herein, CeVWTi catalysts doped with varying amounts of bismuth sulfate (Bi 2 (SO 4 ) 3 ) were synthesized and evaluated for their activity and alkali resistance. These catalysts were characterized using XPS, BET, SEM, H 2 ‐TPR, NH 3 ‐TPD, and XRD techniques. The optimal doping level of Bi 2 (SO 4 ) 3 was 1 wt.%. The NO conversion rate of the catalyst co‐doped with Ce and Bi was 71.6% under the reaction conditions of 300 °C, gas hour space velocity (GHSV) = 200,000 h −1 with a gas composition of 550 ppm NO, 550 ppm NH 3 , 5.6% O 2 , and N 2 as the balance. The NO conversion efficiency of the Bi 0.01 CeVWTi catalyst was maintained at 90.7% after the addition of 1 wt.% KCl poisoning under the reaction conditions of 350 °C, GHSV = 200,000 h −1 , 550 ppm NO, 550 ppm NH 3 , 5.6% O 2 , and N 2 as the balance. Characterization showed that, despite the reduction in the specific surface area of the catalyst and some acidic sites due to Bi doping, the redox performance of Bi 0.01 CeVWTi was significantly enhanced. The excellent redox performance was maintained even after KCl poisoning.
Source: ChemistrySelect
Authors: Tianzhu Shao, Qi Wang, Jiahao Wei, Gonggang Sun, Xinbao Li
Institution: China Jiliang University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: bronze
Award: G6800665418
OpenAlex ID: W4408747728