Multiscale Synergistic Strengthening-Toughening Mechanisms in Lanthanum Oxide-Modified Coiled Tubing Welding Wire Deposited Metal

Year: 2025

Type: article

Abstract: With the increasingly demanding service conditions of coiled tubing, its welded joints require superior synergistic strength-toughness properties to meet comprehensive mechanical performance requirements. This study achieved synergistic optimization of strength and toughness in deposited metal via lanthanum microalloying technology and elucidated microstructural evolution mechanisms and fracture failure mechanisms via multi-scale characterization techniques. The results demonstrate that lanthanum oxide addition effectively modifies inclusion characteristics, inducing phase transformation from O-Mn-Si-Al-Ti to O-Mn-Si-Al-Ti-S-La, with average particle size significantly decreased from 0.19 μm to 0.12 μm. The deposited metal microstructure comprises lath bainite and granular bainite. The addition of 0.5 wt.% lanthanum oxide results in significant microstructural refinement: average grain size decreases from 1.16 ± 1.18 μm to 1.02 ± 1.00 μm, while granular bainite volume fraction decreases from 8.6% to 4.7%. The microstructural optimization also enhances mechanical properties substantially: yield strength increases from 628 ± 14 MPa to 673 ± 12 MPa, and impact toughness improves from 160 ± 6 J to 189 ± 6 J. Mechanistic analysis revealed that proper addition of lanthanum (0.5 wt.%) promotes grain refinement via heterogeneous nucleation and modifies inclusion morphology, effectively inhibiting crack initiation. However, excessive addition (1.0 wt.%) induces inclusion clustering, forming stress concentration sites that degrade mechanical properties.

Source: Metals

DOI: 10.3390/met15040353

Authors: Yuke Yang, Xiaocong Yang, Chengning Li, Xinjie Di

Institution: Tianjin University

Language: English

Topic: Microstructure and Mechanical Properties of Steels

Subfield: Mechanical Engineering

Field: Engineering

Domain: Physical Sciences

SDG: Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $3,137