Lignin-derived cage-like hollow carbon sphere for the catalytic hydrodeoxygenation of vanillin

Year: 2025

Type: article

Abstract: Taking advantages of the structural features of lignin for its functionalization application benefits to develop a sustainable lignin biorefinery process. Herein, cage-like hollow carbon sphere (LC) with high stability and reducibility was fabricated by spray drying and controlled carbonization, due to the high content of carbon element and abundant phenolic hydroxyl groups of lignin. Spray drying would induce the self-assembly of lignin during solvent evaporation, and the introduction of KOH in this process increased the specific surface area of LC and created more surface defects. The controlled carbonization led to the cross-linking of lignin and partly retained the lignin polyphenolic structure, which could be used to adsorb and in situ reduce Pd 2 + to prepare Pd/LC catalyst. Owing to the synergistic catalytic effect of the abundant defect sites on the LC surface and the active Pd sites, the Pd/LC catalyst could catalyze the hydrodeoxygenation of vanillin to 2-methoxy-4-methylphenol under mild reaction conditions (90 °C, 1.5 h, 0.5 MPa H 2 ). Besides, the catalyst showed high activity after four cycles and universality for the other lignin-derived aromatic aldehydes. • Cage-like hollow carbon sphere (LC) with high reducibility was prepared from lignin. • Introduction of KOH during spray drying created more surface defects on LC. • Pd/LC catalysts were synthesized by in situ adsorption and reduction of Pd 2+ on LC. • Pd/LC efficiently catalyzes vanillin hydrodeoxygenation at 90 °C in water.

Source: Industrial Crops and Products

DOI: 10.1016/j.indcrop.2025.120922