Performance analysis of a DC magnetron sputtered Cu2O/TiO2 heterojunction photodetector for short-wavelength detection
Year: 2025
Type: article
Abstract: This study details the fabrication of Cu 2 O/TiO 2 heterostructure thin films via DC magnetron sputtering. The post-annealing temperatures were tuned from room temperature to 250 °C to enhance their UV photodetection capabilities. X-ray diffraction (XRD) analysis confirmed the coexistence of Cu 2 O, CuO, and anatase TiO 2 phases, with improved crystallinity and grain growth occurring at higher annealing temperatures. Field Emission Scanning Electron Microscopy (FESEM) and Atomic Force Microscopy (AFM) analysis showed compact films with progressively increasing surface roughness as the annealing temperature was raised. Optical studies indicated enhanced light absorption due to a reduction in defects and improved crystalline quality. Electrical characterization demonstrated rectifying diode behavior, with annealed devices exhibiting reduced series resistance and enhanced photocurrent under UV illumination. The device annealed at 100 °C demonstrated optimal performance, reaching a responsivity of 0.27 A/W, a detectivity of 4.76 × 10 10 Jones, a linear dynamic range (LDR) of 21.03 dB, and a rise/fall time of 611/620 ms under 395 nm UV illumination. The rapid photoresponse and increased photocurrent at higher bias voltages underscore efficient charge transport at the Cu 2 O/TiO 2 interface. These findings establish Cu 2 O/TiO 2 heterostructures as highly promising materials for advanced UV photodetectors. • CuO/TiO 2 thin films were fabricated via DC sputtering and annealed at varied temperatures. • Annealing enhanced crystallinity and grain growth, improving structural properties. • The device annealed at 150 °C showed the highest UV photodetection performance. • High responsivity (0.26 A/W) and detectivity (5.19 × 10 10 Jones) validate CuO/TiO 2 for UV photodetectors. • Low-temperature processing makes them ideal for industrial UV sensor applications.
Source: Sensors and Actuators A Physical
Authors: Jagadish K A, Dhananjaya Kekuda
Institution: Manipal Academy of Higher Education
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,750
OpenAlex ID: W4408960876