Performance Analysis of Tunnel Water Plugging Engineering Slurry Based on Polycarboxylate Superplasticizer
Year: 2025
Type: article
Abstract: In response to the low efficiency of water plugging slurry in high temperature tunnel engineering, this research explores the optimization configuration of tunnel water plugging slurry. Through the analysis of the gel time, fluidity, stability and mechanical properties of the slurry fused with polycarboxylate superplasticizer, the response surface analysis method and central composite design are used to optimize the design of the slurry for water shutoff projects. Experimental verification showed that the performance of grouting was optimal when the ratio of 12.48 % fast hardening sulfoaluminate cement 425, 0.91 % polycarboxylate superplasticizer, 3.03 ‰ calcium lignosulfonate, and 1.00 ‰ hydroxypropyl methylcellulose was formulated. The gel time of the slurry prepared at 90 ℃ was 12 min, the viscosity was 2064 mPa · s, the water separation rate was 2.87 %, and the compressive strength of the slurry prepared 3 days later was high as 21.35 mPa, meeting the requirements for tunnel water plugging construction. The results showed that fast hardening sulfoaluminate cement 425 had the greatest impact on the performance of the slurry, while polycarboxylate superplasticizer had obvious effects on the stability and flowability of the slurry. The optimal configuration scheme proposed in the study has positive application significance in high surface temperature tunnel water plugging engineering. This optimal solution provides theoretical basis and technical support for tunnel water plugging engineering, and improves the effectiveness of grouting configuration.
Source: Materials Science
DOI: 10.5755/j02.ms.38805
Authors: Daiqiang ZHU, Qiao HE, Hui YANG
Institution: PowerChina (China)
Language: English
Subfield: Civil and Structural Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $539
OpenAlex ID: W4409006534