Achieving superior mechanical and magnetic properties in non-oriented electrical steel with high coherent nanoprecipitation
Year: 2025
Type: article
Abstract: Non-oriented electrical steel strengthened by NiAl–Cu coprecipitates was successfully processed based on strip casting. Equiaxed grains of ∼ 37 µm with strong {411}〈148〉 texture were obtained after annealing. At the aging peak, a high density of nano-coprecipitates with a mean radius of ∼2.8 nm and low lattice misfit of ∼0.66% was formed and exhibited a core–shell structure consisting of a Cu-rich core and a NiAl shell, effectively reducing interface energy and retarding coarsening. Superior mechanical properties with an ultra-high yield strength of 952.4 MPa, magnetic properties with magnetic induction B50 of 1.677 T and iron loss P10/400 of 22.8 W/kg were achieved.
Source: Materials Research Letters
Authors: F. Fang, D. W. Hou, S. F. Dai, Y. X. Zhang, Y. Wang, L. L. Li, X. M. Zhang, G. Yuan, G. D. Wang
Institution: Northeastern University
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,459
Awards: G4690163582, G5426137297
OpenAlex ID: W4409037578