Deterioration mechanism of impact toughness in the coarse-grained heat-affected zone of Ca-treated shipbuilding steel plate with high-Cr content
Year: 2025
Type: article
Abstract: The deterioration mechanism of low-temperature toughness in the coarse-grained heat-affected zone (CGHAZ) of shipbuilding steel plates with Ca-treatment, induced by the addition of Cr, was systematically investigated. Through a combination of experimental research and theoretical calculations, the effects of Cr content (ranging from 0.019 to 0.17 wt%) on microstructural evolution , M 3 C carbide formation, fracture morphology , and low-temperature impact toughness in the CGHAZ were evaluated. The mechanisms responsible for the decline in impact toughness in 170Cr (ω Cr =0.17 wt%) steel have been clarified. Thermodynamic calculations and in situ observations reveal that increasing Cr content reduces the C diffusion coefficient and the austenite-to-ferrite (γ→α) phase transformation temperature. Consequently, there is a decrease in the content of intragranular acicular ferrite (IAF) and an increase in the formation of brittle microstructures within the CGHAZ. It is effectively interpreted by first-principle calculations that the formation energy of M 3 C carbides is reduced when Fe atoms in Fe 3 C are replaced by Cr. The formation energy of Fe 3 C (−0.0487 eV/atom) is greater than that of (Fe, Cr) 3 C (−0.1048 or −0.1111 eV/atom), indicating that the M 3 C type carbides are easier to form in 170Cr steel. In 170Cr steel, strip M 3 C carbides are prone to forming at sub-grain boundaries, weakening the bonding force between sub-grains and making these boundaries more susceptible to crack propagation . Besides, the reduction in the variety of bainite variants decreases the content of high-angle grain boundaries (HAGBs) in bainites, further reducing the crack propagation resistance of 170Cr steel. Furthermore, the increasing C supersaturation in the ferrite of 170Cr steel reduces the plasticity of the CGHAZ, thereby reducing crack initiation energy. In conclusion, the addition of Cr results in a decrease in the low-temperature impact toughness of CGHAZ. As the Cr content increases from 0.019 wt% to 0.17 wt%, the low-temperature impact toughness at −40°C declines from 226 J to 121 J.
Source: Journal of Alloys and Compounds
Authors: Tingting Li, Jian Yang, Yinhui Zhang, Han Sun, Pengfei Hu, Longyun XU
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,660
Award: G6372403050
OpenAlex ID: W4409166227