Effect of Ball Milling Speeds on the Phase Formation and Optical Properties of α-ZnMoO4 and ß-ZnMoO4 Nanoparticles

Year: 2025

Type: article

Abstract: Two modifications of ZnMoO4 were successfully obtained by mechanochemical treatment with two milling speeds applied at 500 and 850 rpm. The phase formation was monitored by XRD analysis. The metastable monoclinic ß-ZnMoO4 was directly synthesized at room temperature using the higher milling speed of 850 rpm. The thermodynamically stable triclinic α-ZnMoO4 was obtained by combining heat treatment t 600 °C and ball milling at the lower milling speed of 500 rpm. The IR spectra contain typical vibration bands and confirm the formation of both ZnMoO4 polymorphs. UV-Vis absorption and photoluminescence (PL) spectroscopy are used to study the optical properties of the as-prepared samples. The calculated optical band gaps for α- and ß-ZnMoO4 are 4.09 and 3.02 eV. The photoluminescence emission spectrum of both samples shows peaks with different maximum intensity at 615 and 403 nm for α and ß phase, respectively. CIE co-ordinates are located in the orange and blue range of the color diagram.

Source: Journal of Manufacturing and Materials Processing

DOI: 10.3390/jmmp9040118

Authors: Maria Gancheva, Reni Iordanova, Petar Ivanov, Aneliya Yordanova

Institutions: Bulgarian Academy of Sciences, Institute of General and Inorganic Chemistry, Institute of Optical Materials and Technologies Jordan Malinowski

Language: English

Topic: Pigment Synthesis and Properties

Subfield: Inorganic Chemistry

Field: Chemistry

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,172

OpenAlex ID: W4409168931

FWCI: 0.434

Cites: 50

Cited by: 2

Related to: 10