Repair Bond Strength and Surface Roughness Evaluation of CAD/CAM Materials After Various Surface Pretreatments
Year: 2025
Type: article
Abstract: This study assessed the repair shear bond strength (SBS; MPa) and surface roughness (Ra; μm) of aged hybrid ceramic (Cerasmart270, GC) and nano-hybrid ceramic (Grandio Blocs, Voco) CAD/CAM blocks after different surface pretreatment methods. In this study, 2 mm thick Cerasmart270 and Grandio Blocs were cut into slabs (Isomet; n = 80 per group). Following aging for six months, the specimens in each CAD/CAM material were randomly divided into four groups (n: 20 each) according to the surface pretreatments: control (no pretreatment), Er:YAG laser, sandblasting, and bur grinding. A total of 10 specimens in each CAD/CAM material pretreatment group were used for Ra evaluation (Perthometer Mahr), while the other 10 were for SBS. After the application of a silane primer (G-Multi Primer, GC) and universal adhesive (G2-Bond, GC), composite build-ups (Filtek Z250; 3MESPE) were performed for the SBS evaluation. After storage in distilled water for 24 h, SBS was evaluated with a universal testing machine (Instron). SBS and Ra data were analyzed with two-way ANOVA and Tukey’s post hoc tests (p < 0.05). SBS was significantly affected by the surface pretreatment methods (p = 0.0001) and by the types of CAD/CAM material (p = 0.005). Bur grinding showed the highest SBS for both CAD/CAM materials, while the control groups yielded significantly lower SBS than bur grinding and sandblasting (p < 0.05). Er:YAG lasers did not significantly enhance the SBS compared to the control group. Sandblasting presented significantly higher SBS than lasers only in Grandio Blocs (p < 0.05). The surface pretreatment methods significantly influenced Ra (p = 0.0001); however, no significant interaction was found between the types of CAD/CAM material and the surface pretreatments (p > 0.05). Control groups exhibited, significantly, the lowest Ra for both materials (p = 0.0001), while no significant differences were observed between the other pretreatment methods. Bur grinding was identified as the most effective pretreatment method for repairing hybrid ceramic CAD/CAM materials.
Source: Coatings
Institution: Yeditepe University
Language: English
Subfield: Orthodontics
Field: Dentistry
Domain: Health Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4409243188