Microstructure and Shear Strength of SiC Ceramics Diffusion Bonded with Ti Foils by Spark Plasma Sintering

Year: 2025

Type: article

Abstract: This study systematically investigated the diffusion bonding of SiC ceramics using Ti interlayers via spark plasma sintering. The effects of holding time (5 min, 10 min, 20 min), joining temperature (1300 °C, 1400 °C, 1500 °C), and Ti foil thickness (5 μm, 10 μm, 20 μm) on joint microstructure and shear strength were characterized through SEM, TEM, XRD, and EDS. The results revealed that the joining temperature was the key factor influencing joint performance, while the holding time and Ti foil thickness had relatively minor effects. When joined at 1300 °C, the primary reaction products in the interlayer consisted of TSC, TiC, and Ti5Si3 phases. Prolonged holding times improved the shear strength, but inhomogeneous phase distribution adversely affected the stability of mechanical properties. In joints with thinner Ti interlayers (5 μm and 10 μm), Si-rich phases tend to aggregate in the central region, leading to stress concentration and reduced joint strength. As the joining temperature increased to 1400 °C and 1500 °C, the Ti5Si3 phase was gradually consumed, and the interlayer primarily contained TSC and TiC phases, leading to a significant enhancement in shear strength, with a maximum value of 127.67 MPa achieved at 1400 °C. These findings provide important experimental evidence and theoretical support for optimizing the joining process of SiC ceramics.

Source: Materials

DOI: 10.3390/ma18081725