Chemical vapour deposition of copper(I) iodide on c-plane sapphire using ethyl iodide and 2-iodo-2-methylpropane
Year: 2025
Type: article
Abstract: In this paper, we report the deposition of copper(I) iodide (CuI) on c-plane sapphire by chemical vapour deposition (CVD). Single crystals of γ -CuI with an out-of-plane orientation of 111, as determined by X-ray diffraction, were grown on the substrate. The copper precursor used was bis(N,N’-di- sec -butylacetamidinato) dicopper(I). Two different iodine precursors, ethyl iodide (EtI) and 2-iodo-2-methylpropane ( t BuI), are discussed in detail. X-ray diffraction and laser scanning microscopy images show the influence of precursor and growth conditions on the morphology and growth rate of CuI. Using t BuI the growth temperature could be lowered and the formation of crystals with flat hexagonal and trigonal shape could be observed. At growth temperatures T growth ≤ 230 °C, another CuI phase in addition to γ -CuI is observed by X-ray diffraction. Photoluminescence measurements show a sharp peak at 380 nm (3.26 eV) that can be assigned to bound excitons of the other CuI phase. • CVD of wide band gap p-type semiconductor γ -CuI on c-plane sapphire. • t BuI and EtI as iodine precursor and [Cu( s Bu-Me-amd)] 2 as copper precursor. • Another CuI phase, grown at low deposition temperatures, is observed. • X-ray diffraction, laser scanning microscopy and photoluminescence spectroscopy.
Source: Journal of Crystal Growth
Institution: Leipzig University
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,110
Funder: Deutsche Forschungsgemeinschaft
OpenAlex ID: W4409423883