High temperature stability of laser additive manufactured stainless steel 316L structures
Year: 2025
Type: article
Abstract: We have investigated the high-temperature behaviour of 316 L stainless steel manufactured using selective laser melting. The microstructure evolution and the corresponding microhardness variation were probed at temperatures from 350 °C up to 1200 °C. Scanning and transmission electron microscopy were used to characterise the grain size, morphology, dislocation structures and porosity in the as-built specimen and after annealing at selected temperatures. The melt pools in the as built specimen exhibited a fine cellular microstructure with average cell size ∼500 nm. The cell structure starts to become unstable at temperatures ≥ 500 °C, leading to slow increase in the cell size as well as a reduction in grain boundary dislocations. At ≥ 800 °C the cell structure completely disappears, together with the local chemical segregations initially present at cell boundaries. Heat treating the material at 1200 °C results in a new equiaxed microstructure with an average grain size of ∼63 µm. The micro-hardness of the as-built specimen was H V = 226, whereas annealing for three weeks at 350 °C reduced the micro-hardness slightly to H V = 216. However, heat treating the sample for one hour at 1200 °C, the micro-hardness significantly decreased to H V = 158. The trend curve for both microstructure and micro-hardness with temperature, exhibited a plateau region in the temperature up to 450 °C, and then sharp variations following the Hall-Petch relation. Heat treatments at higher temperatures resulted the evolution of small pores into larger size as well as extended porosity. This work provides novel insights into the potential of additive manufacturing structures for high-temperature applications. • Thermal stability and hardness of 316 L austenitic steel structures assessed to 1200 °C. • Selective laser melting induces fine cellular structure with average cell size ∼500 nm. • Small increase in cell size and changes in cell boundaries above 500 °C. • Cell structures and chemical segregations at boundaries disappear at 800–900 °C. • Long-term annealing at 350 °C only leads to a small reduction in material’s hardness.
Source: Materials Today Communications
Authors: J. Hou, N. Iqbal, E. Jimenez-Melero
Institutions: University of Manchester, University of Birmingham
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $2,830
OpenAlex ID: W4409429659