Effect of SiCN passivation on electromigration reliability of nanotwinned Cu redistribution lines
Year: 2025
Type: article
Abstract: Nanotwinned Cu (NT-Cu), with numerous advantages, is highly suitable for implementation in Cu redistribution lines (RDLs). However, oxidation is a significant reliability concern as it accelerates resistance increase and shortens the electromigration (EM) lifetime of fine-pitch NT-Cu lines. In this study, bare NT-Cu RDLs exhibited a rapid oxide layer growth, which caused a sharp rise in resistance. To prolong the EM lifespan of NT-Cu RDLs and reduce the thermal budget, plasma-enhanced chemical vapor deposition (PECVD) SiCN was applied to passivate NT-Cu surfaces at a low operating temperature of 150 °C. The SiCN layer effectively inhibited oxidation during EM tests at 200 °C by 1.0 × 10 6 A/cm 2 , resulting in a significant enhancement in the longest EM failure time and mean time to failure (MTTF or T 50 ). The longest EM failure time and T 50 of SiCN-covered NT-Cu lines achieved 4433 h and 1930 h, respectively. Compared to other passivation options, such as TiO 2 , polyimide (PI), and graphene, the SiCN layer demonstrated the highest effectiveness in extending the EM lifetime of NT-Cu lines. This study presents a viable passivation approach for NT-Cu applications and highlights the SiCN coating layer as a superior choice for enhancing the EM reliability of NT-Cu RDLs.
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,640
OpenAlex ID: W4409528456