Fatigue Threshold and Microstructure Characteristic of TC4 Titanium Alloy Processed by Laser Shock

Year: 2025

Type: article

Abstract: Laser shock peening (LSP) is an effective method to improve the fatigue property of metallic materials, and a thorough understanding of its strengthening mechanism is crucial for technology application. In this study, the LSP and fatigue tests of TC4 titanium alloy have been carried out. Combined with the structural characterization and the crystal plasticity finite element (CPFE) simulation, the relationship of stress distribution, microstructure evolution and fatigue performance caused by LSP is revealed. The results indicate that the material’s fatigue life initially increases and subsequently declines with the rising pulse energy. At the optimal pulse energy condition, the laser-shocked specimen demonstrates a 126% increase in fatigue life relative to the untreated specimen, which is accompanied by the higher residual compressive stress along the depth. Meanwhile, the grains become more refined with a uniform size change gradient, and the β phase content drops from 4.1% to 2.2%. Notably, regions with <1-21-0> crystal orientation can be selectively achieved. With the favorable <1-21-0> slip direction orthogonal to the applied fatigue loading axis, the generation and propagation of dislocations are effectively constrained, thereby significantly enhancing the material’s fatigue performance. The stress distribution and fatigue life in models with different grain sizes and phase contents are further analyzed by the CPFE method, showing good consistency with the experimental results. Theoretically, the excessively high pulse energy causes the transient temperature (1769 °C) to surpass the melting point (1660 °C), which can affect the recrystallization structure and stress distribution.

Source: Metals

DOI: 10.3390/met15040453

Authors: Sixin Zha, Heng Zhang, Jiong Yang, Zhen Zhang, Xinxin Qi, Qun Zu

Institution: Hebei University of Technology

Language: English

Topic: Surface Treatment and Residual Stress

Subfield: Mechanical Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $3,137

Funders: National Natural Science Foundation of China, Beihang University