Glass fiber reinforced nylon-6/nylon-1012 composite material serves as automotive rearview mirror bracket
Year: 2025
Type: article
Abstract: In this study, nylon-6/nylon-1012 (PA6/PA1012) composites with varying glass fiber contents were prepared via twin-screw extrusion. The compatibility of PA6/PA1012 was significantly enhanced by the incorporation of 1.5 % ethylene-octene copolymer-grafted-maleic anhydride (POE-g-MAH), as evidenced by SEM analysis demonstrating uniform dispersion of PA1012 within the matrix. The addition of glass fiber (up to 30 wt%) led to a substantial enhancement in tensile strength, flexural strength, and thermal deformation temperature by 153 %, 305 %, and 275 %, respectively, in comparison with pure PA6. The optimized composite exhibited a melt flow index of 26.7 g/10 min (260°C/2.16 kg), which is significantly higher than that of ABS/ASA by 180 %, thereby enabling efficient molding of complex components. Moreover, the incorporation of anti-UV additives (UV-234/HS-944) resulted in the retention of over 79.3 % of impact strength after 500 h UV ageing, surpassing the performance of conventional ABS/ASA. The composite's low equilibrium water absorption (1.20 %) and high dimensional stability (HDT= 210 °C) underscore its suitability for automotive rearview mirror brackets. This study presents a novel strategy for the development of high-performance composites through interfacial optimization and functional additive design. Glass fiber reinforced nylon 6 and 1012 samples with different content were prepared. Compatibility of the PA6/PA1012 was greatly improved by addition of POE-g-MAH. Addition of PA1012 and glass fiber reduces the water absorption, which greatly improved the dimensional stability of the rearview mirror bracket in the later use. 30 % glass fiber reinforced nylon 6 and 1012 presents excellent comprehensive performance. Modified nylon 6 and 1012 meets the application requirements of rearview mirror bracket. • Glass fiber reinforced nylon 6 and 1012 samples with different content were prepared. • Compatibility of the PA6/PA1012 was greatly improved by addition of POE-g-MAH. • The dimensional stability of the rearview mirror bracket in the later use was improved. • 30% glass fiber reinforced nylon 6 and 1012 had excellent comprehensive performance. • Modified nylon 6 and 1012 meets the application requirements of rearview mirror bracket.
Source: Next Materials
Authors: Guolong Wang, Lucheng Li, Peng Yang, Jun Chen
Institution: Jiangxi University of Science and Technology
Language: English
Subfield: Polymers and Plastics
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,280
Awards: G2035830855, G6287479584, G8412664457
OpenAlex ID: W4409595641