Breakdown-induced directional cracking in kilovolt-class β -Ga2O3 (001) vertical trench Schottky barrier diodes

Year: 2025

Type: article

Abstract: Breakdown in kilovolt-class β-Ga2O3 (001) vertical Schottky barrier diodes is often observed with material cracking and local delamination along the [010] direction, which coincides with the orientation of plate-like nanopipe defects in Ga2O3 crystals. This study aims to determine whether these defects are the main cause of device breakdown/failure. Laser confocal and scanning electron microscopy techniques were employed to image original defects in the material and the locations of damage induced upon electrical breakdown at 3.8 kV in the devices. Our analysis shows no clear correlation between the defect locations and the breakdown sites. Failure/cracking along the [010] direction appears to be a consequence of thermo-mechanical failure along the (100) cleavage planes due to arcing-induced damage and the instantaneous heat generated during breakdown, rather than the original plate-like nanopipes, at least for the majority of cases observed.

Source: Applied Physics Letters

DOI: 10.1063/5.0260734

Authors: Sai Charan Vanjari, Aditya K. Bhat, Haiqi Huang, Matthew D. Smith, James W. Pomeroy, Martin Kuball

Institution: University of Bristol

Language: English

Topic: Ga2O3 and related materials

Subfield: Electronic, Optical and Magnetic Materials

Field: Materials Science

Domain: Physical Sciences

Open Access status: hybrid

Funder: Engineering and Physical Sciences Research Council

Award: Transforming Net Zero with Ultrawide Bandgap Semiconductor Device Technology (REWIRE)