Interface reaction constructs iron and phosphorus functionalized zeolite endowing EP with excellent fire safety and mechanical properties
Year: 2025
Type: article
Abstract: High performance epoxy resin (EP) has a wide range of applications, but it still faces problems of high fire hazard and low mechanical properties. However, the development of high performance EP composites with excellent flame retardancy and mechanical properties remains a challenging task. In this work, a novel phosphorus and iron functionalized natural zeolite flame retardants (Zeolite@PFe) was developed for preparation of high-performance flame resisting EP. Compared with pure EP, the flammability and smoke release of EP/Zeolite@PFe composites were greatly reduced. After adding 5 wt% Zeolite@PFe, the EP composites achieved V-0 grade with an LOI of 33.1%. Meanwhile, the total heat release and total smoke release of EP composites were reduced by 22.31% and 36.74%, respectively. Zeolite@PFe exhibited high flame retardance through catalytic carbonization, free radical quenching and physical barrier effect. Notably, the tensile strength and elongation at break of EP increased by 29.7% and 58.84%, respectively, due to the good dispersibility and interfacial interaction between Zeolite@PFe and EP matrix. Therefore, this study provides a novel methodology for the development of EP composites with excellent flame retardancy and mechanical properties.
Source: Chemical Engineering Journal
Authors: Qihao Sun, Shanshan Chen, Xiaolong Chen, Linan Dun, Yuanhao Wang
Institutions: Northeastern University, Shenzhen Polytechnic University
Language: English
Subfield: Polymers and Plastics
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,830
OpenAlex ID: W4409650790