Preparation of New Vanadium Base Composite Conversion Coating on 6061 Aluminum Alloy Surface for Sports Equipment
Year: 2025
Type: article
Abstract: The 6061 aluminum alloy is a commonly used metal material for sports equipment but is vulnerable to the external environment and corrosion. A novel V-Zr-Ti composite conversion coating was successfully prepared on the surface of 6061 aluminum alloy, and a thorough investigation was conducted into the effect of the conversion parameters. Furthermore, the microstructure of the conversion coating, element contents of the coating surface, and dynamic evolution characteristics of the conversion solution were systematically investigated, and furthermore, the relationship among them was established. The results show that the optimal conversion time (CTI) and conversion temperature (CTE) for the VZrCC are 12 min and 45 °C. The VZrTiCC can gradually fill surface scratches during the coating-forming process, resulting in a relatively flat and even surface morphology. The conversion element contents on the VZrTiCC surface demonstrated a gradual increase, and the deposition rate was characterized by high Ti, medium Zr, and low V. The phase of the coating is predominantly constituted by metal oxides derived from conversion compositions, with a minor proportion of fluoride. Furthermore, the VZrTiCC can significantly enhance the corrosion resistance of an Al alloy matrix due to its low icorr and average corrosion rate (ACR), and its corrosion resistance is about 5 times higher than that of the Al alloy matrix. Eventually, the formation process of the VZrTiCC with three key stages was proposed. In subsequent studies, to further establish a composition design framework for the conversion coating, a silane aqueous solution will be added to the existing V-Zr-Ti conversion solution, and a systematic study will be conducted on the V–organic composite conversion coating using computational molecular dynamics simulation combined with experimental characterization.
Source: Coatings
Authors: Yiqun Wang, Xuzheng Qian, Feng Huang, Yingsong Fang
Institution: Huangshan University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4409806527