Fracture resistance of a second generation of zirconia implants after artificial ageing: An in vitro study
Year: 2025
Type: article
Abstract: OBJECTIVES: The aim of this study was to determine the bending moments of a further developed generation of a one-piece zirconia implant system, which, for example, has a reduced diameter in the neck area compared to the predecessor model. METHODS: A total of 48 one-piece ceramic implants with diameters of 3.6 mm and 4.1 mm were included. After preparation of the abutments of 50 % of the implants, 32 out of the 48 implants were subjected to artificial ageing in a chewing simulator (Force: 98 N; 1.2 or 5 million loading cycles; thermocyclicing: 5 °C / 55 °C). The implants were then subjected to static loading until fracture in order to determine the maximum load forces to calculate the bending moments. RESULTS: Implants tested after 1.2 million loading cycles exhibited the highest bending moments (3.6 mm diameter without abutment preparation: 496.1 ± 50.6 Ncm; 3.6 mm diameter with abutment preparation: 507.9 ± 53.5 Ncm; 4.1 mm diameter without abutment preparation: 612.5 ± 49.0 Ncm; 4.1 mm diameter with abutment preparation: 656.9 ± 26.8 Ncm). In contrast, unloaded implants showed the lowest values (3.6 mm diameter without abutment preparation: 443.0 ± 38.6 Ncm; 3.6 mm diameter with abutment preparation: 436.1 ± 42.8 Ncm; 4.1 mm diameter without abutment preparation: 570.3 ± 64.8 Ncm; 4.1 mm diameter with abutment preparation: 560.9 ± 51.5 Ncm), while implants subjected to 5 million cycles of loading showed bending moment values between these two groups. CONCLUSIONS: Within the limits of the present study, preparation of the abutment did not appear to have a negative effect on stability. Also, artificial ageing did not seem to have a negative effect on the fracture resistance; a possible negative effect on the bending moment would have to be investigated with >5 million loading cycles. The measured maximum fracture loads were generally higher than the masticatory forces described in the literature. CLINICAL SIGNIFICANCE: The investigated zirconia implants seem to be a viable alternative to titanium implants.
Source: Journal of Dentistry
Language: English
Subfield: Oral Surgery
Field: Dentistry
Domain: Health Sciences
Open Access status: hybrid
Estimated APC paid: $4,160
OpenAlex ID: W4409859746