Year: 2025
Type: article
Abstract: This paper presents an experimental study of uniform and variable texture patterns on a honed EN-GJS 400-15 spheroidal graphite cast iron surface. Textured samples were fabricated using a CNC electrochemical jet machining technique and tested against a 52100 G5 roller countersurface featuring a rectangular 1 mm × 13 mm contact area. Tribological tests were conducted in a fully flooded PAO4 lubricant bath at 30 °C on a TE-77 reciprocating sliding tribometer with a 25 mm stroke length. Frictional behaviour was assessed at test frequencies from 12 to 18 Hz under two loads, 11 N and 50 N, covering mixed and hydrodynamic lubrication regimes. Experimental results demonstrated that EJM textured surfaces were accurately fabricated within a ±2.50 µm standard error in depth, with chemical etching effects reducing the Rq roughness of initial grinding marks by 0.223 µm. Textured surfaces exhibited a more pronounced friction performance at 50 N than at 11 N, exhibiting a consistent friction reduction of up to 18.8% compared to the untextured surface. The variable textured surface outperformed the uniform textured surface under the mixed lubrication regime due to the enhanced secondary lubrication effect. Optical and SEM analyses revealed that textured surfaces reduced plastic deformation and two-body abrasion.
Source: Lubricants
Authors: Peng Jiang, Jonathon Mitchell-Smith, John Christopher Walker
Institution: University of Southampton
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4410039435