Preparation and Electrochemical Characteristics of the Co-Doped Li7La3Zr2O12 Solid Electrolyte with Fe3+ and Bi3+

Year: 2025

Type: article

Abstract: Solid-state electrolytes (SSEs) have emerged as the most promising alternative to liquid electrolytes in batteries due to their enhanced stability and safety. Among these, the garnet-type Li7La3Zr2O12 (LLZO) solid electrolyte has attracted significant research interest due to its wide electrochemical stability window and good air stability. However, the ionic conductivity of LLZO is lower due to its high sintering temperature and unstable phase structure. In this study, Li6.4+xFe0.2La3Zr2−xBixO12 (x = 0, 0.05, 0.1, 0.15) solid electrolytes were synthesized using a conventional solid-state reaction method by co-doping LLZO with Fe3+ and Bi3+ ions. Compared with pure LLZO, doping with Fe3+ effectively stabilizes the cubic phase, thereby enhancing the ionic conductivity. Moreover, Bi3+ doping significantly lowers the sintering temperature of the electrolyte, which in turn reduces energy consumption during the processing. The co-doping of Fe3+ and Bi3+ not only improves the density of the LLZO electrolyte, achieving a relative density of up to 95%, but also increases the ionic conductivity, with a maximum value of 7.57 × 10−4 S·cm−1 observed at the optimal composition (Li6.4+xFe0.2La3Zr2-xBixO12, x = 0.1).

Source: Molecules

DOI: 10.3390/molecules30092028

Authors: Jialu Qu, Xingyu Duan, Ke Xue, Shengli An

Institutions: Inner Mongolia University of Science and Technology, Guizhou University

Language: English

Topic: Advanced Battery Materials and Technologies

Subfield: Electrical and Electronic Engineering

Field: Engineering

Domain: Physical Sciences

SDG: Affordable and clean energy

Open Access status: gold

Estimated APC paid: $3,258