Abstract: This study investigates the effects of varying lime saturation factors (KH = 0.85, 0.87, 0.90, 0.92) on the mineral composition and hydration behavior of low-heat Portland cement (LHC) clinker, providing theoretical guidance for its industrial production. X-ray diffraction (XRD), scanning electron microscopy (SEM), and hydration heat tests were employed to analyze the phase composition, microstructure, and hydration characteristics of the clinker. The results indicate that as KH increases, the C₃S content rises while the C₂S content decreases, leading to a significant increase in hydration heat peak values and cumulative heat release, as well as enhanced compressive strength. When KH = 0.90, the 7-day hydration heat reaches 276.8 J/g, and the 28-day compressive strength is 43.5 MPa, meeting the GB/T 200-2017 standard for low-heat cement (≤260 J/g) while exhibiting excellent mechanical performance.
Authors: Jiankai Ji, Mifeng Gou
Institution: Henan Polytechnic University
Language: English
Subfield: Civil and Structural Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
OpenAlex ID: W4410081554