Enhancing energy harvesting capabilities using lead-free, flexible piezoelectric poly (vinylidene fluoride) tapes

Year: 2025

Type: article

Abstract: Poly(vinylidene fluoride) (PVDF) has been widely investigated as an energy harvesting material not only for its piezoelectric properties but also for being flexible, lead-free piezoelectric properties, and processing versatility. To enhance its piezoelectric performance, in this study, an additive was blended with PVDF to facilitate the crystalline transformation from α-phase to β-phase. This study explores the influence of two manufacturing processes, extrusion (EX) and compression moulding (CM), and the influence of different stretching and polarization conditions on the piezoelectric performance of PVDF tapes for their integration into a cantilever beam for energy harvesting applications. The heat stretching process for EX and CM tapes was conducted at distinct temperatures (80º and 120 ºC) and stretching speeds (300 and 10 mm/min), leading to different stretch ratios (3.0 and 4.50) that effectively raised the β-phase. Structural changes in the crystalline phases were identified using X-ray diffraction and Fourier transform infrared spectroscopy. Following this, the dipoles were oriented in the direction of an applied electric field (400-500 kV/cm). The piezoelectric performance was characterized by d 33 values, and peak-to-peak voltage, under sinusoidal tensile stress, was obtained using a universal tensile testing machine. A d 33 value of 25-30 pC/N and a peak-to-peak voltage of 27-35 V were obtained. Additionally, the piezoelectric behaviour was observed by arranging the tapes in a cantilever made of fibreglass composite and subjecting it to vibrational excitation at the resonance frequency. Maximum values of output voltage of 12 V for each tape were obtained under cantilever fixture.

Source: Polymer Testing

DOI: 10.1016/j.polymertesting.2025.108838

Authors: Amanda Melo, David Esteves, Ignacio Ezpeleta, Cintia Mateo-Mateo, Nelson Durães

Institution: Asociación de Investigación Metalúrgica del Noroeste

Language: English

Topic: Dielectric materials and actuators

Subfield: Biomedical Engineering

Field: Engineering

Domain: Physical Sciences

SDGs: Affordable and clean energy, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $3,370