In Vitro Evaluation of the Mechanical Properties of Posterior Adhesive Restorations Fabricated Using Three Different Techniques

Year: 2025

Type: article

Abstract: This study evaluates the optical properties and mechanical durability of adhesive restorations fabricated using different techniques for the treatment of single-tooth loss in the posterior region after an aging process. Sixty extracted human teeth (thirty molars and thirty premolars) were restored using three different fabrication methods: 3D-printed resin restorations, fiber mesh-reinforced direct composite restorations, and indirect composite restorations. Color stability was assessed using a spectrophotometer, and fracture resistance was measured using a universal testing machine. Finite element stress analysis (FEA) was conducted to validate mechanical test results under simulated intraoral conditions. The fiber-reinforced composite group exhibited the highest fracture resistance (1057.91 MPa), while 3D-printed restorations showed the lowest (p < 0.05). Regarding color stability, the fiber-reinforced group demonstrated the highest ΔE00 values (ΔE00 = 1.71), differing significantly from the other groups, while the 3D-printed and indirect composite restorations showed no significant difference. Mechanical test results were consistent with FEA findings. These results indicate that fiber reinforcement enhances mechanical durability in high-load-bearing areas, while 3D-printed restorations may not yet be suitable for posterior regions. However, their potential use in anterior restorations, where occlusal forces are lower, warrants further investigation to improve material properties.

Source: Polymers

DOI: 10.3390/polym17101340

Authors: Cem Peskersoy, Gozde Acar

Institution: Ege University

Language: English

Topic: Dental materials and restorations

Subfield: Orthodontics

Field: Dentistry

Domain: Health Sciences

SDG: Good health and well-being

Open Access status: gold

Estimated APC paid: $3,258