Synergistic Toughening Mechanisms in ZrO2/Multi-Walled Carbon Nanotubes-Reinforced CaZr4(PO4)6 Ceramics for Enhanced Mechanical Performance

Year: 2025

Type: article

Abstract: ZrO2 and multi-walled carbon nanotubes (MWCNTs) were selected as single-phase and composite toughening agents to investigate the influence on the mechanical properties of CaZr4(PO4)6 (CZP) ceramics. The results revealed that the addition of single-phase or composite toughening agents had minimal impact on the phase composition and crystallinity of CZP ceramics. When the content of the single-phase ZrO2 toughening agent reached 10 wt.%, the flexural strength of CZP ceramics increased to 71.60 MPa due to the particle toughening mechanism of ZrO2. With the addition of 1.0 wt.% ZrO2 and 0.3 wt.% MWCNTs, the CZP ceramics demonstrated enhanced densification and improved sintering activity. The small-sized ZrO2 particles were evenly dispersed within the ceramic matrix, accompanied by a phase transformation during sintering. Together with MWCNTs, this combination resulted in a significant increase in flexural strength, reaching 138.43 MPa. An in-depth analysis of the toughening mechanisms indicated that the CZP ceramic matrix primarily featured ZrO2 phase transformation toughening and the pull-out and bridging toughening provided by MWCNTs. The synergistic interaction of these multiple toughening mechanisms significantly enhanced the mechanical properties of CZP ceramics, providing valuable theoretical insights for optimizing the performance of phosphate ceramics in practical applications.

Source: Materials

DOI: 10.3390/ma18102289