α-amino acid-derived polyamidoamines as photostabilizers for cotton
Year: 2025
Type: article
Abstract: • α-Amino acid-based polyamidoamines were studied as cotton photostabilizers. • PAA-impregnated cotton strips underwent accelerated photoaging under UVA-UVB exposure. • Colorimetric analysis allowed ranking photostability of COT/PAA samples. • All PAAs effectively protected cotton from UV-exposure except for the tyrosine-based copolymer. Arginine- (M-ARG), glycine- (M-GLY), serine- (M-SER), histidine- (M-HIS) and tyrosine/arginine- (M-TYR 30 -ARG 70 ) derived polyamidoamines (PAAs) were studied as cotton photostabilizers. Cotton strips with a 6 wt.% PAA add-on were subjected to accelerated photoaging in a solar chamber under UVA–UVB exposure at 40% relative humidity and 30–35 °C. Colorimetric analysis was conducted at 15-minute intervals during irradiation. Virgin cotton exhibited significantly more yellowing than PAA-treated fabrics, except for those treated with M-TYR 30 -ARG 70 . Scanning electron microscopy revealed slight surface erosion on untreated cotton (COT) fibers after prolonged UV exposure, whereas PAA-treated cotton (COT/PAA) showed uniform PAA coatings with only minor surface wrinkles and localized fractures. Colorimetric analysis enabled ranking the photostability of COT/PAA samples as follows: COT/M-ARG > COT/M-GLY > COT/M-SER > COT/M-HIS > COT > COT/M-TYR 30 -ARG 70 . These results demonstrate that all PAAs enhanced UV protection, except for M-TYR 30 -ARG 70 . Nuclear magnetic resonance analysis of PAA coatings extracted from photoaged cotton showed no detectable structural degradation. The results confirm that α-amino acid-derived PAAs effectively protect cotton from photoaging, although formulations containing UVB-absorbing residues exhibit increased susceptibility to irradiation. The effectiveness of PAAs was attributed to the radical scavenging activity of tert-amine groups and the side-chain residues within their repeat units.
Institution: University of Milan
Language: English
Subfield: Building and Construction
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,190
Funder: Università degli Studi di Milano
OpenAlex ID: W4410539651