D24. Analysis of Nanoparticulate Shedding of Silicone Breast Implant Shells
Year: 2025
Type: article
Abstract: PURPOSE: The etiology of breast implant-associated pathologies not caused by rupture remain poorly understood. Particulate shedding is a recognized phenomenon of silicone breast implants and hypothesized to perpetuate chronic peri-implant inflammation. Prior research quantifying particulate size focuses on the microparticle range (>1μm). As recent technological advancements permit interrogation of the nanoparticle (NP) range (<1μm), we sought to examine nanoparticulates released from commercial implant shells. METHODS: Silicone textured and smooth implant shells from Allergan™ and Mentor™ were thoroughly cleaned, sterilized, cut to line individual wells within a 96-well plate, and incubated in serum-free cell culture media for 48 hours. This ‘conditioned’ media (CM) was collected from textured (TCM) and smooth (SCM) implant shells and analyzed through the NanoSight Pro Nanoparticle Tracking Analyzer (Malvern Panalytical, Malvern, UK). RESULTS: No NPs were detected in serum-free media. NPs were detected in all implant CM groups, with greater mean concentration in TCM (Allergan: 2.09x109 particles/mL, Mentor: 2.69x109) by over one order of magnitude compared to SCM (Allergan: 1.19x108, Mentor: 4.18x107). Median NP size was smaller in CM from textured Allergan and Mentor (126 and 141nm, respectively) compared to their smooth counterparts (152 and 185nm, respectively). TCM NP size distributions peaked between 100-200nm, while SCM NP histograms spanned more broadly across smaller sizes with additional peaks between 600-1,000nm. CONCLUSION: Breast implant shells incubated in media release nanoparticulates, with textured shells shedding over 10x more NPs than smooth. Further study is required to determine what, if any, role NPs play in inducing breast implant pathology, including BIA-ALCL.
Institution: Weill Cornell Medicine
Language: English
Subfield: Surgery
Field: Medicine
Domain: Health Sciences
Open Access status: gold
Estimated APC paid: $2,195
OpenAlex ID: W4410640840