Fabrication of hybrid nanostructured Bi2S3/Si heterojunction photodetector by laser ablation in thiourea

Year: 2025

Type: article

Abstract: This work reports on the fabrication of a high-performance Bi 2 S 3 /Si visible photodetector by laser ablation of Bi target in thiourea without using a catalyst. The structural, morphological, optical, and electrical properties of Bi 2 S 3 colloids are studied. The X-ray diffraction pattern reveals that the synthesized Bi 2 S 3 is crystalline with an orthorhombic structure. An increase in laser energy density leads to improved crystallinity. Scanning electron microscopy investigation of the Bi 2 S 3 confirms the formation of several morphologies: porous fibrous (PFs), nanoparticles (NPs), and nanorods (NRs), depending on the laser energy density. The optical energy gap of Bi 2 S 3 nanostructures was found to decrease from 1.85 to 1.74 eV as the laser energy density increased from 9.55 to 15.92 J/cm 2 . Hall measurements show that the electrical conductivity and electron mobility of Bi 2 S 3 decreases with an increase in laser energy density. The fabricated Bi 2 S 3 /Si photodetectors exhibit figures of merit that depend on the laser energy density. The optimum photodetector, fabricated at a laser energy density of 15.92 J/cm 2 , was found to have a responsivity of 1.32 A/W and an external quantum efficiency of 480 % at 350 nm. The rise/fall time ratio for the photodetector fabricated at 15.92 J/cm 2 was 0.34/0.34 s.

Source: Journal of Science Advanced Materials and Devices

DOI: 10.1016/j.jsamd.2025.100919

Authors: Ahmed M. Ahmed, Asmiet Ramizy, Raid A. Ismail, Nasir A. Ibrahim, Vajid Nettoor Veettil, M.H. Eisa

Institutions: University of Anbar, University of Technology - Iraq, Imam Mohammad ibn Saud Islamic University

Language: English

Topic: Laser-Ablation Synthesis of Nanoparticles

Subfield: Biomedical Engineering

Field: Engineering

Domain: Physical Sciences

SDG: Affordable and clean energy

Open Access status: gold

Estimated APC paid: $1,300