Study on the Properties of Solidified Silt Based on Microbially Stimulated Recycled Hardened Cement Powder

Year: 2025

Type: article

Abstract: The carbon emissions from the cement industry account for approximately 8% of global carbon emissions, which exerts significant pressure on the environment. In this paper, the microbial-induced calcium carbonate precipitation (MICP) technology was introduced into the carbonization modification research of recycled hardened cement powder (RHCP), and the carbon sequestration performance of RHCP under different pressures was studied. The physicochemical properties of the carbonated products were characterized by microscopic testing methods, and the carbon sequestration mechanism under different pressures was obtained. Subsequently, carbonated RHCP (C-RHCP) was tested as a partial cement substitute for solidified sludge to evaluate its mechanical and durability properties. The results show that when the pressures were 0.3 and 0.5 MPa, the carbon sequestration capacity of RHCP was relatively good, reaching 59.14 and 59.82 g/kg, respectively. Since the carbon sequestration amounts under the two pressures were similar, and considering the energy consumption, in this study, a reaction pressure of 0.3 MPa was selected to prepare C-RHCP. Compared with pure cement, the 28-day unconfined compressive strength (UCS) of the sludge cured with 30% C-RHCP increased by 12.08%. The water stability coefficient of the solidified sludge in the C-RHCP group was greater than 1 after soaking for 7, 14, and 21 days, while the water stability coefficient of the cement group decreased to 0.92 at 14 days. After 20 freeze-thaw cycles, the mass losses of the cement group, the RHCP group, and the C-RHCP group were 31.43%, 38.99%, and 33.09%, respectively. This research not only provides an environmentally friendly strategy for the resource utilization of RHCP but also pioneers a new synergistic model that combines microbial mineralization with the modification of industrial solid waste. It demonstrated significant scientific value and engineering application prospects in reducing carbon emissions in the cement industry and promoted sustainable geotechnical engineering practices based on the "waste-waste" principle.

Source: Materials

DOI: 10.3390/ma18112575

Authors: Xihui Yin, Chuanjiang Tian, Jintao Hong, Qiwei Zhan, Xinyu Wang, Wanying Dong

Institutions: China Communications Construction Company (China), Jiangsu University of Science and Technology, Southeast University

Language: English

Topic: Microbial Applications in Construction Materials

Subfield: Environmental Engineering

Field: Environmental Science

Domain: Physical Sciences

SDGs: Responsible consumption and production, Climate action, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $3,137