Microstructure evolution and mechanical properties of cold rolled Ti–Mo precipitation-hardened stainless steels after ageing treatment

Year: 2025

Type: article

Abstract: While cold deformation prior to aging is a well-established approach for enhancing the mechanical properties of precipitation-hardened stainless steels (PHSSs), the synergistic effect of cold deformation and aging on microstructural evolution remains insufficiently explored. To investigate this effect, different levels (35 % and 70 %) of cold deformation strain (CDS) were applied, followed by aging at low (520 °C) and high (640 °C) temperatures, leading to variations in the formation of reverted austenite within the Ti–Mo PHSS. Regardless of the CDS, reverted austenite was observed only when aging was performed at 640 °C, while no significant austenite reversion occurred at 520 °C. Therefore, only aging was conducted at 640 °C, the trade-off relationship between strength and ductility improved with increasing CDS. This improvement was primarily due to the simultaneous formation of a higher density of η-Ni 3 Ti precipitates and reverted austenite during aging. These results indicate that optimizing metallurgical parameters can further enhance the mechanical performance of Ti–Mo PHSS, particularly by leveraging the effects of cold deformation strain and aging temperature on austenite reversion and precipitation behavior.

Source: Journal of Materials Research and Technology

DOI: 10.1016/j.jmrt.2025.06.041

Authors: Yu-Shan Chang, Chih-Yuan Chen

Institution: National Taipei University of Technology

Language: English

Topic: Microstructure and Mechanical Properties of Steels

Subfield: Mechanical Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $1,640

Funders: Ministry of Science and Technology of the People's Republic of China, Ministry of Science and Technology, Taiwan