Fabrication of Graphene-reinforced Alumina Ceramic Composites via Adsorption-precipitation Self-assembly Combined with Spark Plasma Sintering
Year: 2025
Type: article
Abstract: ：Alumina ceramics are widely utilized structural materials, yet their inherent brittleness and monofunctionality limit their application in high-stress scenarios.The strategic integration of two-dimensional graphene sheets, characterized by their excellent mechanical, thermal and electrical properties, into ceramic matrix can facilitate grain refinement through interface engineering, thereby achieving performance optimization.Conventional physical blending methods result in poor uniformity and integrity of 2D sheets, thereby impeding advancements in graphene-ceramic composites.Herein, a novel adsorption-precipitation self-assembly (APSA) method was proposed for the nondestructive integrating of graphene oxide (GO) sheets with submicron Al2O3 particles.A homogeneous precursor is obtained by uniform deposition of Al 3+ ions adsorbed on GO surface, followed by low-temperature rapid densification via spark plasma sintering (SPS).For the resultant composites, the incorporated graphene is aligned parallel to the alumina grains, facilitating grain refinement and significantly enhancing the mechanical properties through the synergistic effect of various toughening mechanisms, including pull-out, crack extension, and bridging.In comparison to monolithic alumina ceramics, the ceramic composites exhibit a 43% enhancement in flexural strength ((428±87) MPa) and a 34% improvement in fracture toughness ((4.40±0.13)MPa⋅m 1/2 ).Furthermore, the strength and toughness values are also increased by 15% respectively, compared to specimens made from the conventional ball-milling mixing process, confirming the efficacy and advancement of such manufacturing approach.
Source: Journal of Inorganic Materials
DOI: 10.15541/jim20250140
Authors: Aopeng CHENG, Yuewen WANG, Wentao XU, Quanwei LIU, Haitao ZHANG, Youfu ZHOU
Language: English
Subfield: Ceramics and Composites
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
Awards: G2345764966, G8680093024
OpenAlex ID: W4411187206