The Influence of Water Content in Ethylene Glycol Electrolyte on Magnesium Plasma Electrolytic Fluorinated Coating
Year: 2025
Type: article
Abstract: Plasma electrolytic fluorination (PEF) of AZ31 magnesium alloy was carried out by adding different ratios of water to the ethylene glycol-ammonium fluoride electrolyte. The structural composition of the coatings was characterized using SEM, XRD, and EDS, and the effects of water content on the microstructure and corrosion resistance of the PEF coatings were analyzed. The results showed that the addition of water promoted the ionization of ammonium fluoride and increased the conductivity of the glycol electrolyte, which led to a decrease in the termination voltage. However, the coating thickness was not changed by the addition of water. The O element in water was not enough to compete with the F element in the electrolyte and had a small effect on the PEF coating composition, which was still dominated by MgF2. The addition of water had an effect on the structure of the coating: with an increase in water content, the number of coating penetration holes decreases, and the continuity is enhanced. The pores on the surface of the coating tended to be levelled off and transitioned to the typical coating structure of PEO (plasma electrolytic oxidation). The addition of water to the glycol electrolyte was conducive to improving the corrosion resistance of the coatings. The corrosion resistance of PEF coatings in neutral NaCl corrosive medium firstly increased and then decreased, and the strongest corrosion resistance was obtained when the ratio of glycol and water is 6:4.
Source: Coatings
Authors: Yifeng Yang, Hao Wang, Xuchen Lu, Cancan Liu
Institution: Nanjing Tech University
Language: English
Subfield: Biomaterials
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,137
OpenAlex ID: W4411217329