Drilling Machinability of Glass, Basalt, and Hybrid Epoxy Composites: Thrust Force, Thermal Load, and Hole Quality
Year: 2025
Type: article
Abstract: The drilling machinability of glass fiber G14, basalt fiber B14, and two hybrid laminates (B4G6B4, G4B6G4) was evaluated through 36 full-factorial experiments employing an HSS-G drill, three spindle speeds (715, 1520, 3030 rpm), and three feed rates (0.1–0.3 mm rev−1). Peak thrust force varied from 65.8 N for B14 at 0.1 mm rev−1 to 174.3 N for G14 at 0.3 mm rev−1; hybrids occupied the intermediate range of 101–163 N. Infra-red thermography recorded maximum drill temperatures of 110–120 °C for G14, almost double those of B14, while both hybrids attenuated hotspots to below 90 °C. ANOVA attributed 73.4% of thrust force variance to feed rate, with material type and spindle speed contributing 15.5% and 1.7%, respectively; for temperature, material type governed 41.5% of variability versus 17.0% for speed. Dimensional quality tests revealed that the symmetric hybrid G4B6G4 maintained entrance and exit diameters within ±2% of the nominal 6 mm, whereas B4G6B4 over-expansion exceeded 8% at the lowest feed and G14 exit diameters grew to 6.1 mm at 0.3 mm rev−1. Integrating basalt compliance with glass stiffness, therefore, halves thrust force relative to G14, suppresses delamination and overheating, and offers a practical strategy to prolong tool life and improve hole quality in multi-material composite structures. These insights guide parameter selection for lightweight hybrid composites in aerospace, renewable-energy installations, and marine components worldwide.
Source: Polymers
Institutions: Kocaeli Üniversitesi, Sakarya University
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,258
Funder: Kocaeli Üniversitesi
Award: G8133125355
OpenAlex ID: W4411256399