Enhanced Corrosion Resistance and Cytocompatibility of Magnesium Alloys with Mg(OH)2/Polydopamine Composite Coatings for Orthopedic Applications

Year: 2025

Type: article

Abstract: A critical barrier to the clinical translation of biodegradable magnesium (Mg)-based materials lies in their rapid degradation rate in physiological environment, which leads to premature structural failure and compromised cytocompatibility. Micro-arc oxidation (MAO) coatings offer preliminary corrosion mitigation for Mg alloys, while their inherent structural porosity compromises long-term durability in physiological environment. To address this limitation, we developed a hierarchical coating system consisting of a dense Mg(OH)2 interlayer (MAO/HT) superimposed on the MAO-treated substrate, followed by a functional polydopamine (PDA) topcoat to create a MAO/HT/PDA composite architecture. The surface characteristics and crystalline structures of these coatings were systematically characterized using field-emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD). The corrosion resistance and interfacsial stability in physiological environment were quantitatively assessed through electrochemical analyses and long-term immersion tests in simulated body fluid (SBF). The cytocompatibility of the coatings was assessed by directly culturing osteoblast on the coated samples. The results reveal that the Mg(OH)2 film possesses a bulk-like structure and effectively seals the micro-pores of the MAO coating. The current density of MAO/HT/PDA sample decreases by two orders of magnitude compared to that of MAO sample, indicating excellent corrosion resistance. The PDA layer not only acts as a strong barrier to improve the corrosion performance of the coating but also helps maintain the stability of the coating, thus delaying coating destruction in SBF. Moreover, the osteoblast culture results suggest that the MAO/HT/PDA coating promotes cell spread and proliferation noticeably compared to both the MAO and MAO/HT coatings. This study provides compelling evidence that the Mg(OH)2/PDA composite coating is biodegradable and offers outstanding protection for micro-arc oxidized magnesium. As a result, it holds great promise for significant applications in the field of orthopedic medicine.

Source: Coatings

DOI: 10.3390/coatings15060729

Authors: Chunlin Li, Boqiong Li, Wenxia Yan

Institutions: Jinzhong University, Shanxi Medical University, Shanxi Academy of Medical Sciences

Language: English

Topic: Magnesium Alloys: Properties and Applications

Subfield: Biomaterials

Field: Materials Science

Domain: Physical Sciences

SDG: Good health and well-being

Open Access status: gold

Estimated APC paid: $3,137