Internal curing using modified superabsorbent polymers: Dual optimization of shrinkage mitigation and mechanical performance
Year: 2025
Type: article
Abstract: Superabsorbent polymers (SAP) show significant promise in mitigating autogenous shrinkage in high-performance concrete (HPC), although their tendency to reduce compressive strength remains a persistent challenge. This study investigates SAPs synthesized from distinct monomer types (acrylic acid, acrylamide, and an acrylic acid-acrylamide copolymer), varying degrees of cross-linking, and the incorporation of active additives, to quantitatively assess their performance characteristics. The study further examines the impact of SAP on autogenous shrinkage, microstructural evolution, and the mechanical properties of SAP-modified cement pastes. Results indicate that polyacrylamide-based SAPs exhibited superior water retention compared to both polyacrylic acid-based SAP and acrylamide-co-acrylate SAP, with enhanced retention capacity corresponding to the degree of cross-linking. This property improved the efficient use of internal curing water, thereby reducing autogenous shrinkage in the cement paste. Additionally, the active additives were found to effectively reduce residual pore size following SAP water release, thereby enhancing the mechanical performance of the paste. A positive correlation was observed between the concentration of active additives in SAP and improvements in the structural integrity of the cement paste. The polyacrylamide-based SAP with 9 wt% cross-linking and 50 wt% Nano-SiO2 loading (SAP-NSc) exhibited the best overall performance. Compared to polyacrylic acid-based SAP and acrylamide-co-acrylic acid SAP, SAP-NSc demonstrated superior suppression of autogenous shrinkage while significantly mitigating the adverse effects of SAP on the mechanical properties of cement pastes. Relative to SAP-free cement pastes, the SAP-NSc modified formulations achieved reductions in 7-day autogenous shrinkage of 96.5% and 89.7%, respectively, with compressive strength variations of -8.7% and +12.6% after 91 days. These results highlight the promising potential of SAP-NSc as an advanced internal curing material for HPC applications.
Authors: Chenhao He, Fulong Fan, Yuanshuai Wu, Lifang Wang, Hongtao Tao, Jian Huang, Lin Chi, Yanchao Zhu, Xiaodong Wen, Yang Lv, Xiangguo Li
Language: English
Subfield: Civil and Structural Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,540
Awards: G5265114642, G861164914
OpenAlex ID: W4411454415