APDBD Plasma Polymerized PNIPAm Coatings with Controlled Thickness via Spin Coating Technique

Year: 2025

Type: article

Abstract: Thermosensitive Poly(N-isopropylacrylamide) (PNIPAm) films were synthesized via atmospheric pressure dielectric barrier discharge (APDBD) plasma polymerization. In order to control the thickness of the films, a spin coating technique was used during the deposition of N-isopropylacrylamide (NIPAM) monomer solution onto several glass substrates. We used the coefficient of determination (R-square value) in linear regression to investigate the significance and optimize spin coating parameters during the fabrication of NIPAM coatings before exposure to APDBD plasma to ensure reproducible and uniform film properties. The spin coating parameters investigated in this study include spin speed, spin time, and NIPAM solution concentration with R-square values of 0.978, 0.946, and 0.944, respectively. Also, as a result of the thermosensitive nature of NIPAM, the spin coating operating conditions of temperature and humidity were maintained at 39.0 °C and 15%, respectively. During the APDBD plasma polymerization, argon was used as the discharge gas, and the distance between the two parallel electrodes and plasma frequency were maintained at 5.0 mm and 17 kHz, respectively. The plasma exposure time required for polymerization of PNIPAm coatings was optimized to 60 s. Also, the results showed that a coating with minimal defects had an optimal thickness of 5.18 μm, fabricated under conditions of 90 wt.% NIPAM concentration, spin speed of 4000 rpm, and total spin time of 7 s.

Source: Coatings

DOI: 10.3390/coatings15070762