Effect of Ti content on ablation behavior and mechanism of C/C-(Zr,Hf,Ti)C composites under oxyacetylene flame above 2600 °C
Year: 2025
Type: article
Abstract: C/C-(Zr,Hf,Ti)C composites were prepared via reactive melt infiltration adopting Zr-Hf-Ti mixed powder with different content of Ti (0 at%, 10 at%, 20 at% and 30 at%) as infiltrant. The influence of titanium content on the microstructure and ablation resistance of the composites was investigated after exposing to oxyacetylene flame at temperatures exceeding 2600 °C. Results showed that the most suitable content of Ti was 20 at%. This composition exhibited optimal ablation resistance, demonstrating a linear ablation rate of 3.5 μm/s and mass ablation rate of 1.5 mg/s. Compared with C/C-(Zr,Hf)C composites (0 at% Ti), these values were reduced by 53 % and 84 % respectively, which can be attributed to the formation of a dense (Zr,Hf,Ti)O 2 protective oxide layer that effectively protected the underlying (Zr,Hf,Ti)C layer.
Authors: Junwen Liu, Yalei Wang, Zhiwei Qiao, Xiang Xiong, Ziwei Wang, Zhiyong Ye, Yanbin Wei
Institution: Central South University
Language: English
Subfield: Ceramics and Composites
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,640
Awards: G2017630972, G5019009909
OpenAlex ID: W4411966350