Incorporating bulk microstructural and surface properties to predict the performance of high chromium cast irons – indentation behaviour and wear performance

Year: 2025

Type: article

Abstract: This study investigates the indentation behaviour and wear performance of two hypoeutectic high chromium cast iron alloys with 16% and 26% chromium. Indentations were performed using an alumina spherical ball at various loads, and the resulting contact radii (ranging from ∼ 30 μm to 50 μm) were compared with Hertzian predictions. A novel methodology using image segmentation was developed to estimate bulk mechanical properties using local phase distribution. Plasticity index calculations, incorporating both matrix and carbide surface characteristics, yielded comparable values (∼ 29) for both alloys, indicating similar elastic-plastic contact responses despite differences in carbide size and volume fraction. Abbott-Firestone curve analysis revealed that 26% Cr alloy exhibited slightly higher bearing capacity at shallow depths. Subsequent wear tests showed that under low load conditions (5 N), the 26% Cr alloy exhibited lower wear rates compared to the 16% Cr alloy. However, at 20 N, the difference falls within the standard deviation, suggesting that both alloys perform similarly under high-load wear.

Source: Journal of Materials Research and Technology

DOI: 10.1016/j.jmrt.2025.07.020

Authors: U. Pranav Nayak, Bruno Alderete, Sebastian Suarez, María Agustina Guitar, Frank Mücklich

Institution: Saarland University

Language: English

Topic: Metal Alloys Wear and Properties

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $1,640

Funders: Deutscher Akademischer Austauschdienst, Deutsche Forschungsgemeinschaft