Erosion of AISI 4340 and AISI 8620 Steels with High Ductility Caused by SiC Particles

Year: 2025

Type: article

Abstract: In this study, solid particle erosion tests were conducted to evaluate the resistance of AISI 4340 (EN24) and 8620 alloy steels against silicon carbide (SiC). These steels were selected due to their high hardness, yield strength (σy), ultimate tensile strength (σuts) and elongation (%), which are significant parameters, influencing wear resistance. An erosion rig based on the ASTM G76-95 standard was used to perform the testing. Tests were carried out using different impact angles, 30°, 45°, 60° and 90°, with a particle velocity of 24 ± 2 m/s. The abrasive flow rate was 0.7 ± 0.5 g/min and the temperature was between 35 °C and 40 °C. Characterization techniques such as SEM were employed to identify the chemical composition of AISI 4340 and AISI 8620 steels and optical microscopy to determine the morphology of SiC abrasive particles. In addition, the SiC particle size was between 350 and 450 µm; it was determined by the particle size distribution technique. SEM micrographs were obtained to classify the wear mechanisms, characterized by micro-cutting, micro-ploughing, grooves, pitting actions and embedded particles on the surface at 30° and 90°. The results showed that AISI 8620 steel exhibited higher erosion resistance than AISI 4340 steel. Finally, AFM was used to evaluate the roughness variations before and after erosion tests, specifically in the central zone of the wear scars at 30° and 90° for both materials.

Source: Metals

DOI: 10.3390/met15070800